aços maraging

Os Aços Maraging Júlio C. O. Lopes
Ciência e Tecnologia dos Materiais, Vol.19, nº 1/2, 2007
OS AÇOS MARAGING
JULIO C. O. LOPES,
Instituto de Logística da Aeronáutica, Subdivisão de Ensino Presencial,
Av. Monteiro Lobato 6365, Cumbica, Guarulhos, São Paulo [e-mail] ABSTRACT: This paper reports a developments and recent researches of Maraging steel . The mechanical proprieties of this class of steel is very interesting for aeronautical applications speciality for toughness and strength resistence.
The martensitic transformation allow a high density of dislocations in a CBC structure , and this dislocation, will be a preferred site for precipitation during the aging treatment.
The precipitation hardening is responsible about fifty percent of total hardening in this steel grade. For this reason, the real studies are concentrates in the precipitation phenomena. New types of alloys are added to modify the precipitation effect .
Keywords: Maraging, Precipitation, martensite.
RESUMO: Este artigo apresenta informações sobre o desenvolvimento e pesquisas realizadas sobre os aços Maraging. Neste tipo de aço, as propriedades mecânicas são muito interessantes para a aplicação aeronáutica, especialmente nas propriedades de resistência mecânica e tenacidade.
Nestes aços , a transformação martensítica produz uma martensita de estrutura cúbica de corpo centrado com elevada densidade de discordâncias. Estas discordâncias atuam como sítios nucleadores para a precipitação de compostos intermetálicos que ocorre durante o envelhecimento.
O endurecimento por precipitação nestes aços é responsável por aproximadamente cinqüenta porcento do endurecimento total apresentado por este tipo de aço, e é por este motivo que os eforços
Palavras chave: Aços Maraging; Precipitação; Martensita.
1. - HISTÓRICO DE DESENVOLVIMENTO DOS AÇOS
MARAGING
Durante a guerra fria, na década de 50, os EUA procuraram desenvolver um bombardeiro supersônico que pudesse atingir