couro usado no cimento

Quim. Nova, Vol. 34, No. 6, 979-983, 2011

Daniel Véras Ribeiro*, Shih Yung Yuan e Márcio Raymundo Morelli
Departamento de Engenharia de Materiais, Universidade Federal de São Carlos, Rodovia Washington Luis, km 235, 13565-905
São Carlos – SP, Brasil

Artigo

EFEITO DA ADIÇÃO DE SERRAGEM DE COURO TRATADA QUIMICAMENTE NAS PROPRIEDADES DO
CIMENTO PORTLAND

Recebido em 24/8/10; aceito em 21/12/10; publicado na web em 14/3/11

EFFECT OF CHEMICALLY TREATED SHAVE LEATHER ADDITION ON THE CHARACTERISTICS OF PORTLAND
CEMENT PASTES. The sheave leather was subjected to chemical treatment in an attempt to immobilize chromium ion in a matrix of cement. Cementitious pastes were obtained by adding different proportions of waste treated solutions (5 and 10% compared to the cement mass) and the pH and setting time (hardening) were measured. Aiming to check the leather influence in Portland cement pastes, the phases formation were observed by X-ray diffraction (XRD). The results showed that the pretreatment was effective for the waste dissolution and the pH of treated waste chemical solutions did not influence significantly the characteristics of cement paste, with a slight increase in setting time results.
Keywords: shave leather; Portland cement; inertization.

INTRODUÇÃO
O Brasil, segundo maior produtor e quarto maior exportador de couros do mundo (de acordo com o Centro das Indústrias de Curtume do Brasil,1 CICB), tem aumentado sua preocupação no tocante aos problemas associados à geração de resíduos perigosos, tais como a serragem de couro e o grande volume de efluentes líquidos resultantes do processamento das peles, principalmente entre as etapas de ribeira e curtimento (wet blue). Segundo Pacheco,2 o consumo total médio de água nos curtumes brasileiros é de aproximadamente 32 m3 para cada tonelada de pele salgada.
Apesar de o cromo ser adicionado ao processo de curtimento em sua forma trivalente (menos tóxica do que a forma hexavalente, que