Artigo Retard Ncia De Chama Em Poliestireno Efeito Da Adi O De Hidr Xidos Duplos Lamelares De Magn Sio E Alum Nio Por Solubiliza O Em Clorof Rmio

Artigo

Retardância de Chama em Poliestireno: Efeito da Adição de
Hidróxidos Duplos Lamelares de Magnésio e Alumínio por
Solubilização em Clorofórmio
Dominguini, L.;* Pizzolo, J. P; Polla, M. B.; Martinello, K.; Fiori, M. A.
Rev. Virtual Quim., 2014, 6 (4), 1121-1129. Data de publicação na Web: 18 de maio de 2014

http://www.uff.br/rvq
Polystyrene Flame Retardant: Effect of Addition of Layered Double Hydroxides of
Magnesium and Aluminum by Solubilization in Chloroform
Abstract: In this work it was possible to evaluate flame retardant properties of the composite polystyrene PS- layered double hydroxide (LDH) [Mg4Al2(OH)14.3H2O], prepared by addition of the inorganic material via solubilization of polystyrene with chloroform. LDH Mg-Al was synthesized by coprecipitation method and characterized by XRD and laser granulometer. The PS-LDH composite obtained was characterized by FTIR and TGA. The flame retardant effect was determined by comparing the horizontal burning rate of the composite at different concentrations of LDH with pure PS. The results demonstrate that the horizontal burning rate decreases with increasing PS inorganic filler. With about
20 % by weight of layered double hydroxide, the combustion rate halved. Therefore, the technique of PS solubilization in chloroform to addition of the inorganic filler was effective for the production of a composite PS-LDH [Mg4Al2(OH)14.3H2O], with better thermal stability than pure polystyrene.
Keywords: Polystyrene; horizontal burning rate; flame retardancy.

Resumo
Neste trabalho avaliou-se as propriedades retardantes de chama do compósito poliestireno (PS) e hidróxido duplo lamelar (HDL) [Mg4Al2(OH)14.3H2O], preparado por adição do material inorgânico através de solubilização de poliestireno com clorofórmio. O HDL Mg-Al foi sintetizado pelo método de coprecipitação e caracterizado por Difração de Raios-X (DRX) e determinação de tamanho partícula média por granulometria à laser. O compósito PS-HDL foi caracterizado por