COMPORTAMENTO TÉRMICO DA CAULINITA HIDRATADA
José Eduardo Gardolinski, Harley Paiva Martins Filho e Fernando Wypych*
Departamento de Química, Universidade Federal do Paraná, CP 19081, 81531-990 Curitiba - PR
Recebido em 23/11/01; aceito em 28/5/02

THERMAL BEHAVIOR OF HYDRATED KAOLINITE. Well-ordered kaolinite from the Brazilian Amazon Region (State of
Pará) was initially reacted at 60 °C with a water dimethylsulfoxide mixture. After washing and characterisation, the resulting material was washed several times with methanol and in the final step with water. The water molecules displace the previously dimethylsulfoxide intercalated molecules and two different hydrated kaolinites were obtained. An unstable phase characterized by an interplanar basal distance of 0,996 nm that after drying collapse to the stable 0,844 nm hydrated kaolinite. The dehydration of the sample to disordered kaolinite was accompanied by Powder X-ray Diffractometry, thermal analysis (simultaneous TG and
DSC) and FTIR spectroscopy.
Keywords: kaolinite; clay minerals; intercalation compounds.

INTRODUÇÃO
Os argilominerais do grupo da caulinita envolvem quatro variedades politípicas polimórficas, a Nacrita (JCPDS:16-606), Diquita
(JCPDS:10-446), Caulinita (JCPDS:14-164 e 29-1488) e Haloisita
0,7 nm ou metahaloisita (JCPDS:29-1487), todos com a fórmula
Al2Si2O5(OH)4, além da Haloisita 1,0 nm ou endelita (JCPDS:1489) com a fórmula Al2Si2O5(OH)4.2H2O1,2. Tipicamente os argilominerais nacrita, diquita, caulinita e haloisita 0,7 nm ocorrem na forma de cristais tabulares e a haloisita 1,0 nm na forma de tubos ou cilindros, que ocorrem pelo enrolamento das lamelas da caulinita.
Dependendo da sua gênese, a caulinita pode se apresentar com elevada, média e alta ordem estrutural ao longo do eixo “b” da estrutura triclínica (ou monoclínica), sendo baixo o teor de substituintes isomórficos (normalmente Fe+3,+2 no sítio do alumínio),